Ready-to-use, reinforced concrete conglomerate, based on hydraulic lime and granular perlite, for the construction, with only addition of water, of lightweight slabs and screeds, with high thermal and acoustic insulation, for ecological building interventions and in the restoration of vintage buildings and monuments.
Screed material and floor screeds - Screed material - Properties and requirements
Jetëgjatësia: 12 muaj
Përmasa maksimale e agregatit: 2.5 mm
Përzierja me ujë: 25 - 35 %
Pot life: 60 mm
Temperatura e aplikimit: +6 / +30 °C
Lidhja e aderimit
Reagimi ndaj zjarrit
Rezistenca në ngjeshje pas 07 ditësh
Rezistenca në ngjeshje pas 28 ditësh
> 5.0 MPa
Rezistenca në përkulje pas 07 ditësh
Rezistenca në përkulje pas 28 ditësh
> 1.6 MPa
- Gështenjë e hapur
- Qese 13 kg
Approximately 6 kg/m² of SANALIT for every centimetre of thickness to be implemented (approximately 600 kg per cubic metre).
For laying subbase screeds in high performance thermo-acoustic ecological buildings.
Application surfaces should be clean, free of soiling, crumbling and non-adhering parts, dust, etc., conveniently saturated with water until they reach the condition "saturated with dry surface".
Pour about 2/3 of the mixing water into the mixer. Gradually add SANALIT and the water still needed, by mixing until a homogeneous lump-free mixture of the desired consistency is obtained. Support the product at the reference height and float until a smooth and planar surface is obtained, preparing the joints beforehand where necessary. The mixing water indicatively necessary is equal to 65-75% by weight (8.5 -9.5 litres per 13 kg bag).
- Straight edge
- Nënshtresa çimentoje
It is always essential to carry out preliminary tests to check the appropriateness of the product, depending on specific requirements.
Protect fresh surfaces from direct exposure to sunlight, from the rain and the wind, and cure the prolonged moist hardening.
Please note that SANALIT is only intended as a subbase for subsequent cement or lime-based slabs. It should not be used as a top trampling layer.