Thixotropic, reinforced fibre, anti-shrink mortar, slightly expansive in plastic phase, high-performance in terms of resistance and waterproofing characteristics, specific for the compensation of cavities and detachments in roughcast underpinning, and for accurate fixing of wooden or steel beams in masonry whatever its nature.
Jetëgjatësia: 12 muaj
Pot life: 60 min
Trashësia maksimale e lejueshme: 8 cm
Të përdoret me doreza mbrojtëse
Temperatura e aplikimit: +5 / +35 °C
Përzierja me ujë: 12-13 %
Përmasa maksimale e agregatit: 2 mm
Trashësia minimale e lejueshme: 1 cm
Përmbajtja e klururit
< 0.01 %
Rezistenca në përkulje pas 01 ditë
Rezistenca në ngjeshje pas 28 ditësh
Lidhja e aderimit
> 2 MPa
Zgjerimi i kontrastuar me shërimin e ajrit për 1 ditë
> 0.6 mm/m
Rezistenca në ngjeshje pas 01 dite
Përcaktimi i kompaktësisë termike
> 2 MPa
Rezistenca në përkulje pas 28 ditësh
- Qese 25 kg
- Koli: 50 x (Qese 25 kg)
REPAR TIX G2 is based on high-resistance cements, superpozzolanic fillers, plasticisers, stabilisers, and anticorrosive agents, antiallergic additives, selected aggregates. Free of chloride, aluminium, metal powders and aggressive substances in general.
Approximately 19 kg/m² of REPAR TIX G2 for every centimetre of thickness to be implemented (approximately 1900 kg per cubic metre).
Fixing and anchorages of I-beams, clamps, beams, metal structures, reinforcing rods, prefabricated elements etc. Execution of render underpinning, in civilian, industrial, rural and infrastructural building, both for restructuring and newly built.
Application surfaces should be clean, free of soiling, crumbling and non-adhering parts, dust, etc., conveniently saturated with water until they reach the condition "saturated with dry surface". An adequate roughening of the surfaces by scarifying, sandblasting etc. is always necessary in order to obtain the maximum adhesion values to the substrate. The optimal values are obtained with high pressure hydro-scarification. Bare the irons undergoing disruptive oxidation or deeply oxidized, removing the rust of the exposed irons (by sandblasting or abrasive brushes).
Pour about 2/3 of the mixing water into the mixer, add REPAR TIX G2 and the remaining water; continue to mix until a homogeneous lump-free mixture is obtained. The mixing water should be about 12-13% of the weight of the bag. After mixing is completed wait a few minutes before applying.
For high anchoring sections add GHIAIETTO 6.10 (please refer to the appropriate technical data sheet for more information).
- Muratura të përziera
- Muratura me gurë
Adopt laying procedures capable of ensuring the absence of gaps and discontinuities; cure the protection and the prolonged moist hardening of exposed surfaces.